DRILUBE® products for rubber

Applying a coating to rubber, with its high frictional drag, facilitates lubrication of the rubber.
It is also useful in preventing rubber from bonding, due to its non-adhesion property.
The coating moves as the rubber expands and contracts to prevent cracks.

Product name	LM-3	FS-1360	FD-2501	FD-5700	FI-9240	FN-2801	FN-2802
Color tone	Ash Black	Milk White	Milk White	Milk White	Black	Milk White	Milk White
Category	MoS2	PTFE	PTFE	PTFE	PTFE	PTFE	PTFE
Coating method	Spray	Spray	Spray	Spray	Spray	Spray	Spray
Cure temperature	Dry at room temperature	100℃	150℃	100～150℃	150℃	150℃	230℃
time	60min.	60min.	40min.	60min.	60min.	40min.	40min.
Film thickness	5～15µm	5～15µm	5～15µm	5～15µm	5～20µm	5～20µm	5～20µm
Abrasion resistance
Non-adhesion
Resistance to oil

DRILUBE® products for plastics

Depending on the friction conditions, plastic materials can wear easily.
Applying DRILUBE® product coatings to plastics provides stable lubrication and markedly improves their durability.

Product name	FR-3600	FS-1140	P-2000	F-890	FC-5210	LF-1
Color tone	Milk White	Black	Black	Milk White	Green	Black
Category	PTFE	PTFE	PTFE	PTFE	PTFE	PTFE
Coating method	Spray	Spray	Spray	Spray/ Dip	Spray	Spray
Cure temperature	Dry at room temperature	80℃	80℃	Dry at room temperature	150℃	Dry at room temperature
time	80℃ 40min.	40min.	30min.	80℃ 30min.	30min.	80℃ 30min.
Film thickness	5～15µm	5～15µm	5～15µm	1～5µm	5～20µm	5～15µm
Abrasion resistance
Hardness
Non-adhesion

∗If you would like to receive more specific details, please feel free to contact us using the inquiry form.